产品描述
The material of intermediate roll is required to have high thermal shock resistance. The service life of roller is shortened because of peeling and crack caused by cold hardening of roller surface due to high thermal shock resistance of intermediate roll, which is one of the most common problems of intermediate roll. Our company endeavors to design the intermediate roll according to the requisite properties of intermediate roll through the study on material smelting and forging, material selection and special heat treatment technology for the purpose of preventing peeling and crack caused by high thermal shock resistance.
Taking H12 as an example, it has high pressure resistance. The microscopic structure generated by the special heat treatment technology can strengthen tenacity and pressure resistance.
In addition, the intermediate roll made from the latest R8 material and special heat treatment technology has higher pressure resistance and no peeling or crack. The result of compression test is higher than most of intermediate rolls, and the service life is more than two times the common intermediate roll.
| Applicable Roller | Material | Hardness | Material Properties |
|---|---|---|---|
| Intermediate roll | D2(12%Cr) | 58-62HRC | Peeling or crack is caused by higher hardness of roller due to high thermal shock resistance. |
| Intermediate roll | H12 A8(modified)5%Cr | 58-62HRC | Peeling or crack is caused by higher hardness of roller due to high thermal shock resistance. |
关键词：
森吉米尔轧辊 | 多辊轧机轧辊 | 四、六辊轧机轧辊 | 冶金备件
产品询价
移动端二维码
常州瑞科精密轧辊有限公司
地址：江苏省常州市新北区尚德路28号
联系人：周正军(总经理）13585326600
电话：0086-0519-8560-0297
传真：0086-0519-8595-8689
邮编：213125
邮箱：ruikezhagun@czrico.com （ 邮箱登录 ）